Alusong Cladding-NANO

Alusong Cladding-NANO

Alusong Cladding-NANO aluminum composite panel is coated with special NANO PVDF coating with excellent self-cleaning feature. It’s widely used in office buildings, shopping centers, industry building, airports, gas stations, such as air pollution requirements on the high buildings.
分享
0
  • 颜色和表面
  • 产品范围
  • 产品属性
  • 产品应用
  • 技术数据
颜色和表面

ALUSONG NANO coated aluminum composite panels are produced by a new and exciting NANO PAINT technology. A transparent NANO coat is applied over 2 or 3 PVDF coating to enhance the performance of the coated panels weatherability and durability resulting in longer color and glossy retention. The NANO coating  prevents dirt, water, permanent spray paint, carbon monoxide, grease, oil or any foreign particles to penetrate through the paint surface. In addition, the NANO coating is a non-toxic, VOC EMISSION FREE coating system, which makes the surface self –cleaning and repellent to air-borne pollutants.



产品范围
Aluminum alloyAA1100  AA3003 AA5005
Aluminum skin0.21mm,0.30mm,0.35mm,0.40mm,0.45mm,0.5mm
Panel thickness3mm,4mm,5mm,6mm
Panel width1220mm,1250mm,1500mm
Panel length2440mm,3050mm,4050mm
Surface treatmentNANO PVDF
Colors70 colors, RAL & PANTONE colors upon request
Customers sizeaccepted
GLOSSY30%-50%


Panel width: ±2mm        Panel length:±3mm

Panel thickness: ±0.2mm    Panel diagonal: ≤5mm

Aluminum sheet thickness: ±0.01mm


产品属性
Alusong Cladding-NANO

Raw material:

Base material: high strength aluminum alloy sheet

PE core material: non-toxic low density polyethylene

Surface coating: NANO PVDF coating

Back coating: primer coating

Product properties

Excellent easy-cleaning

Pollution resistance

Oil resistance

Good friction resistance

Strong acid & alkali resistance

Outstanding weather resistance


产品应用

1. Wall curtain, Cladding and Facade

2. Hotels and commercial mansions

3. Exterior renovation for old buildings

4. Subway and airports

5. Industry plants and materials,

6. Vehicle and boat materials


  • Application Application
  • Application Application
  • Application Application
  • Application Application
  • Application Application
  • Application Application
技术数据
DescriptionTest standardNANO PVDF
Thickness of coatingPVDF paint≧34um35um to 37um
Coating flexibility (T-bend)Polyester paint≥2T2T
Color differentΔE≦2.0(follow color sample)ΔE<2.0
Pencil hardnessISO 15184:1998 Section 105H
Chemical resistance5%HCI or 5% NaOH test in 24 hours -No changeNo change
Coating adhesionISO 15184:1998 Section 6The edges of the cut are completely smooth,none of the square of the lattice is detached.
Resist solventNo change for 200 times(MEK)No change
Boiling water resistanceEN438-2:2005 Section 12Rating 5,no visible change.Average change of mass: 0.08%;Average change of thickness:1.36%
Peeling strength/stripping strengthBS EN319:19932.4N/mm2
Impact test for paintISO6272-1:2002 Section 8The coating not crack or peel after 2kg weight ball dropped from 1.5m height
Abrasion resistance (L/Mil)ISO7784-2:1997 Section 8The abrasive rubber wheel: Taber H-22; the cycles number:100; the mean loss mass:91mg
Temperature resistanceEN438-2:2005 Section 19Rating 4, change of gloss only
Coefficient of linear Thermal ExpansionISO11359-2;1999 Section 71.3x10-4K
Detergent resistance (3%)ASTM D2248No change
Humidity Resistance (3000hrs,100%RH,100°F)ASTM D2247No change
Salt spray resistance (3000hrs,5% salt)ASTM B117No change
Resistance to StainingEN438-2:2005 Section 26Rating 5,no visible change